TS846-TDS high temperature small particle wear

TS846-TDS high temperature small particle wear

TS846 high temperature small particle wear resistant coating is a modified high temperature resistant epoxy resin, ceramic microspheres and superhard crystals and other components of the epoxy adhesive. After curing, the coating is firmly attached to the substrate, resistant to fine particles in high temperature conditions, erosion and friction loss, the maximum temperature resistance up to 250℃; excellent. High temperature resistance, impact resistance and good corrosion resistance

1.Typical uses:

Suitable for repair and prevention of wear and tear on material transfer equipment or general load grinding and erosion equipment under high temperature conditions. Used in power plants, cement factories, steel mills, aluminum oxide factories, dust removal equipment, powder selection machines, powder discharge machines, boiler ignition systems, etc.

2.Pre-curing characteristics:

  
      A component characteristic
      Typical values
    
      Appearance
      Grey
    
      Chemical composition of paste ceramic microsphere filler material
      Modified high temperature resistant epoxy density (g/cm3)
      2.30
    
      B component characteristic
      Typical values
    
      Appearance
      Gray-black
    
      Chemical composition of paste ceramic microsphere filling base material
      Modified amine compound density (g/cm3)
      2.30

A component characteristic	Typical values
Appearance	Grey
Chemical composition of paste ceramic microsphere filler material	Modified high temperature resistant epoxy density (g/cm3)	2.30
Appearance	Gray-black
Chemical composition of paste ceramic microsphere filling base material	Modified amine compound density (g/cm3)	2.30

3. Mixing characteristics:

  
      Mixing Characteristics
      Typical values
    
      Appearance
      Dark grey
    
      Weight Ratio
      A:B=2.2:1
    
      Volume Ratio
      A:B=2.2:1
    
      Coverage Area
      6900 cm² @ 6.3 mm
    
      Coating/10 Kg Shelf Life (min)
      180 (100g @ 25℃)
    
      Full Load Curing Time
      Room temperature 24h + 100℃ 3h

Mixing Characteristics	Typical values
Appearance	Dark grey
Weight Ratio	A:B=2.2:1
Volume Ratio	A:B=2.2:1
Coverage Area	6900 cm² @ 6.3 mm
Coating/10 Kg Shelf Life (min)	180 (100g @ 25℃)
Full Load Curing Time	Room temperature 24h + 100℃ 3h

4. After curing characteristics

  
      After Curing Characteristics
      Typical Values
    
      Density (g/cm3) (GB/T13354-1992)
      2.3
    
      Hardness (Shore D) (GB/T2411-1980)
      85
    
      Shear Strength (MPa) (GB/T7124-1986)
      12
    
      Compressive Strength (MPa) (GB/T1041-1992)
      120
    
      Operating Temperature (℃)
      -25 to 250