TS838-TDS fast solid large particle wear

TS838-TDS fast solid large particle wear

TS838 fast solid large particle wear resistant coating is a special modified epoxy resin, ceramic ball and superhard crystal composition of two component epoxy adhesive. Suitable for mixing and scraping construction, sizing does not collapse, can be easily in the top surface, vertical and complex surface construction; Suitable for low temperature environment Curing and short downtime maintenance; The solidified coating is firmly attached to the substrate, resistant to the impact and erosion of coarse particle pulp, and has excellent performance different impact resistance and good high temperature resistance

1.Typical uses:

It is suitable for repair and prevention of equipment with high load, abrasive wear and erosion wear. Used in the ore processing system of mines, smelting plants, bending pipe, rotary liquid separator, centrifuge.

2.Pre-curing characteristics:

  
    A component characteristic
    Typical values
  
    appearance
    grey
  
    Chemical composition of paste ceramic microsphere filling base material
    Density of modified epoxy resin (g/cm3)
  
    2.30
  
    B component characteristic
    Typical values
  
    appearance
    ash black
  
    Chemical composition of paste ceramic microsphere filling base material
    Modified amine adduct
  
    Density (g/cm3)
    2.10

A component characteristic	Typical values
appearance	grey
Chemical composition of paste ceramic microsphere filling base material	Density of modified epoxy resin (g/cm3)
	2.30
B component characteristic	Typical values
appearance	ash black
Chemical composition of paste ceramic microsphere filling base material	Modified amine adduct
Density (g/cm3)	2.10

3. Mixing characteristics:

  
    Mixing characteristics: Typical values
  
    Appearance
    dark grey
  
    Weight ratio
    A:B=2.3:1
  
    Volume ratio
    A:B=2:1
  
    Coating
    7380cm2@6.3mm
  
    Coating /10Kg Application period
    20 (100g@25℃)
  
    Minimum curing time at room temperature before
    (h@25℃
  
    50% load   
    6
  
    100% load   
    10

Mixing characteristics:	Typical values
Appearance	dark grey
Weight ratio	A:B=2.3:1
Volume ratio	A:B=2:1
Coating	7380cm2@6.3mm
Coating /10Kg Application period	20 (100g@25℃)
Minimum curing time at room temperature before	(h@25℃
50% load	6
100% load	10

4. After curing characteristics

  
    After curing characteristics:
    Typical values
  
    Density (g/cm3) (GB/T13354-1992)
    2.3
  
    Hardness (邵氏 D) (GB/T2411-2008)
    85
  
    Searing strength (MPa) (GB/T7124-2008)
    8
  
    Compressive strength (MPa) (GB/T1041-2008)
    89
  
    Operating temperature (℃)
    -60 to 160