TS816-TDS small particle wear resistant

TS816-TDS small particle wear resistant

TS816 small particle wear resistant coating is a two-component epoxy adhesive cured at room temperature. This product is a special modified epoxy resin and wear-resistant ceramic microspheres. Composed of composite materials. Good operation, suitable for complex surface and thin coating, reduce the time of parking maintenance. After curing the coating with the base. Solid body attachment, with excellent wear resistance, impact resistance and good high temperature resistance

1.Typical uses:

It is suitable for the repair and prevention of the equipment of abrasive and erosion wear under the condition of high temperature pneumatic transmission material or general load. Used in power plants, cement, steel mills, aluminum oxide plant dust removal, powder sorting machine, powder discharging machine, boiler ignition system, etc

2.Pre-curing characteristics:

  
    A component characteristic
    Typical values
  
    Appearance
    Gray
  
    Chemical composition of base material filled with paste like ceramic microspheres
    Density of modified high temperature resistant epoxy resin (g/cm3) 2.30
  
    B component characteristic
    Typical values
  
    Appearance
    Dark gray
  
    Chemical composition of base material filled with paste like ceramic microspheres
    Density of modified amine adduct (g/cm3) 2.30

A component characteristic	Typical values
Appearance	Gray
Chemical composition of base material filled with paste like ceramic microspheres	Density of modified high temperature resistant epoxy resin (g/cm3) 2.30
B component characteristic	Typical values
Appearance	Dark gray
Chemical composition of base material filled with paste like ceramic microspheres	Density of modified amine adduct (g/cm3) 2.30

3. Mixing characteristics:

  
    Mixing characteristics
    Typical values
  
    Appearance
    Dark grey
  
    Weight ratio
    A:B=2.2:1
  
    Volume ratio
    A:B=2.2:1
  
    Coating area
    6900cm2@6.3mm
  
    Applicable period(min)
    180(100g@25℃)
  
    Curing time required at full load
    Room temperature 24 H + 100 ℃ 3 h

Mixing characteristics	Typical values
Appearance	Dark grey
Weight ratio	A:B=2.2:1
Volume ratio	A:B=2.2:1
Coating area	6900cm2@6.3mm
Applicable period(min)	180(100g@25℃)
Curing time required at full load	Room temperature 24 H + 100 ℃ 3 h

4. After curing characteristics

  
    After curing characteristics
    Typical values
  
    Density (g/cm3) (GB/T13354-1992)
    2.3
  
    Hardness (邵氏 D) (GB/T2411-2008)
    85
  
    Searing strength (MPa) (GB/T7124-2008)
    12
  
    Compressive strength (MPa) (GB/T1041-2008)
    120
  
    Operating temperature (℃)
    -25 to 250