TS836 TDS fast - setting small particle wear

TTS836 TDS fast - setting small particle wear

TS836 TDS fast - setting small particle wear

TS836 is a two-component epoxy adhesive composed of special modified epoxy resin, ceramic microspheres and superhard crystals.Suitable for mixing and scraping construction, sizing does not collapse, can be convenient in suspended, vertical and complex surface construction; Suitable for low temperature environment curing and

Short-time downtime maintenance; After curing, the coating is firmly attached to the substrate, resistant to the impact of fine particles, erosion wear, cavitation abrasion, and has excellent resistance.Wear and impact resistance and good high temperature resistance

1.Typical uses:

It is suitable for the repair and prevention of pneumatic abrasive wear and cavitation wear equipment at low temperature. Used in dust removal, dust collection system, air separation equipment, separator, cyclone, water pump, collector inner wall and rotary parts of wear resistance repair and prevention.

And can be used to paste ceramic sheet at the base of the work; Used in powder dressing, ore dressing, power plant, cement plant, port and ship transport system.

2.Pre-curing characteristics:

  
    A component characteristic: 
      Typical values
  
    Appearance
    Filling of gray paste ceramic microspheres
  
    Chemical composition of base material
    The density of modified epoxy resin (g/cm3) was 2.20
  
    B component characteristic: 
      Typical values
  
    Appearance
    Gray black paste ceramic microsphere filling base material
  
    Chemical composition
    Modified amine adduct density (g/cm3) 1.95

A component characteristic:	Typical values
Appearance	Filling of gray paste ceramic microspheres
Chemical composition of base material	The density of modified epoxy resin (g/cm3) was 2.20
B component characteristic:	Typical values
Appearance	Gray black paste ceramic microsphere filling base material
Chemical composition	Modified amine adduct density (g/cm3) 1.95

3. Mixing characteristics:

  
    Mixing characteristics: 
      Typical values
  
    Appearance
    dark grey
  
    Weight ratio
    A:B=2.5:1
  
    Volume ratio
    A:B=2.2:1
  
    Coating
    738cm2@6.3mm
  
    Coating / 1000g shelf life (min)
    20 (100g@25℃)
  
    50% load  
    6
  
    100% load:
    12

Mixing characteristics:	Typical values
Appearance	dark grey
Weight ratio	A:B=2.5:1
Volume ratio	A:B=2.2:1
Coating	738cm2@6.3mm
Coating / 1000g shelf life (min)	20 (100g@25℃)
50% load	6
100% load:	12

4. After curing characteristics

  
    After curing characteristics
    Typical values
  
    Density (g/cm3) (GB/T13354-1992)
    2.1
  
    Hardness (邵氏 D) (GB/T2411-2008)
    85
  
    Searing strength (MPa) (GB/T7124-2008)
    18
  
    Compressive strength (MPa) (GB/T1041-2008)
    90
  
    Operating temperature (℃)
    -60-160