TS3498-TDS-1 epoxy backing adhesive
TS3498-TDS-1 epoxy backing adhesive
TS3498 epoxy backing adhesive is a kind of low viscosity, easy to mix and pour high-performance epoxy adhesive; Good low temperature casting and curing
Performance; After mixing, it is poured between the crusher lining plate and the cone to realize seamless filling and bonding. Effectively support the liner and body after curing,
Realize buffer, energy absorption, shock absorption, high load impact resistance, excellent performance; Environmental protection, safety, convenient construction, long service cycle, high efficiency and cost ratio
1.Typical uses:
It is mainly used for shock absorption and buffering between cone, rotary crusher, lining plate of ball mill and body. Also used for ship stern tube, shafting pad block fixed, mining equipment, machine tool base installation leveling. It can also be used for stone, concrete and steel structure bonding and metal railing implantation. It can be used in mining and smelting plant, water and electricity, road building, building materials, garden and other industries.
2.Pre-curing characteristics:
| A component characteristic | Typical values |
|---|---|
| Appearance | Light blue viscous liquid |
| Chemical composition of base material | Viscosity of modified epoxy resin (MPa. S) 20000 |
| (Brookfleld HB3#转子 5rpm) | (GB/T2794-1995) |
| B component characteristic | Typical values |
| Appearance | Light yellow viscous liquid |
| Chemical composition of base material | Viscosity of epoxy modified amine adduct (MPa. S) 1500 |
| (Brookfleld LV 2#转子 12rpm) | (GB/T2794-1995) |
3. Mixing characteristics:
| Mixing characteristics: | Typical values |
|---|---|
| Appearance | wathet |
| Weight ratio | A:B=91: 9 |
| Applicable period(min) | 10 |
| Minimum curing time at room temperature before operation (H) | 8 |
4. After curing characteristics
| Characteristics after curing | Typical values |
|---|---|
| Density (g/cm3) (GB/T13354-1992) | 1.65 |
| Hardness (邵氏 D) (GB/T2411-2008) | 85 |
| Searing strength (MPa) (GB/T7124-2008) | 20 |
| Compressive strength (MPa) (GB/T1041-1992) | 110 |
| Bending strength (MPa) (GB/T9341-2000) | 50 |
| Operating temperature (℃) | -60-180 |
Related contents
-
TS846-TDS high temperature small
-
TS838-TDS fast solid large particle wear
-
Thread locking and sealing anaerobic
-
TS3495-TDS-1 epoxy backing adhesive
-
TS3498-TDS-1Epoxy backing adhesive
-
TS818-TDS large particle wear resistant adhesive
-
2216（HT216）Wear Resistant Repair
-
TS816-TDS small particle wear resistant adhesive