TS3495-TDS-1 epoxy backing adhesive

TS3495-TDS-1 epoxy backing adhesive

TS3495 epoxy backing adhesive is a high performance epoxy adhesive cured at room temperature. After mixing, it is poured between the crusher lining plate and the machine body to achieve seamless filling Filling and bonding; After curing, it can effectively support the liner and the body to achieve buffer, Energy absorption, shock absorption, high load impact resistance, excellent performance; Environmental protection and safety, Convenient construction, long service cycle, high efficiency and cost ratio

1.Typical uses:

It is mainly used for shock absorption and buffering between cone, rotary crusher, lining plate of ball mill and body. Also used for ship stern tube, shafting pad block fixed, mining equipment, machine tool base installation leveling. It can also be used for stone, concrete and steel structure bonding and metal railing implantation. It can be used in mining and smelting plant, water and electricity, road building, building materials, garden and other industries.

2.Pre-curing characteristics:

  
    A component characteristic
    Typical values
  
    Appearance
    Light blue viscous liquid
  
    Chemical composition of base material
    Viscosity of modified epoxy resin (MPa. S) 40000 
  
    (Brookfleld HB3#转子 5rpm)
    (GB/T2794-1995)
  
    B component characteristic
    Typical values
  
    Appearance
    Colorless transparent liquid
  
    Chemical composition of base material
    Viscosity of epoxy modified amine adduct (MPa. S) 15  
  
    (Brookfleld LV 2#转子 30rpm)
    (GB/T2794-1995)

A component characteristic	Typical values
Appearance	Light blue viscous liquid
Chemical composition of base material	Viscosity of modified epoxy resin (MPa. S) 40000
(Brookfleld HB3#转子 5rpm)	(GB/T2794-1995)
B component characteristic	Typical values
Appearance	Colorless transparent liquid
Chemical composition of base material	Viscosity of epoxy modified amine adduct (MPa. S) 15
(Brookfleld LV 2#转子 30rpm)	(GB/T2794-1995)

3. Mixing characteristics:

  
    Mixing characteristics: 
      Typical values
  
    Appearance
    wathet
  
    Weight ratio
    A:B=100:6.9
  
    Volume ratio
    A:B=9.5:1
  
    Applicable period(min)    
    10
  
    100% load:
    8

Mixing characteristics:	Typical values
Appearance	wathet
Weight ratio	A:B=100:6.9
Volume ratio	A:B=9.5:1
Applicable period(min)	10
100% load:	8

4. After curing characteristics

  
    Characteristics after curing
    Typical values
  
    Density (g/cm3) (GB/T13354-1992)
    1.7
  
    Hardness (邵氏 D) (GB/T2411-2008)
    85
  
    Searing strength (MPa) (GB/T7124-2008)
    20
  
    Compressive strength (MPa) (GB/T1041-1992)
    112
  
    Bending strength (MPa) (GB/T9341-2000)
    50
  
    Operating temperature (℃)
    -60-180